Wire Drawing Dies

I.Carbide Grade for Wire Drawing Dies

Grade	Density(g/cm3)	Hardness(HRA)	TRS(MPa)	Applications   recommended
YG6X	14.95	91.5	1800	For drawing steel and nonferrous wires or bars of less than ￠6.00mm under not so much stress.
YG6	14.95	90.5	1900	For drawing steel and nonferrous alloy bars of less than ￠20.00mm under more stress and also for drawing tubes of less than ￠10.00mm.
YG8	14.8	89.5	2200	For drawing steel and nonferrous bars and tubes, also for manufacturing mechanical parts, tools and wear parts.
YG10	14.5	88.5	2400
YG15	14	87	2800	For drawing steel bars and tubes with a high reduction rate and for manufacturing anvils, drilling and punching and impacting.

*Can produce the drawing dies according to client’s grade requirement.

II.Size information for Carbide Drawing Dies

Types	I.D range	Types	I.D range	Types	I.D range
D12*8	φ1.0-φ1.8	D40*25	φ1.0-φ21	D95*32	φ2.0-φ46
D13*10	φ1.0-φ2.6	D45*27	φ1.0-φ23	D100*33	φ2.0-φ51
D15*10	φ1.0-φ3.8	D50*27	φ1.0-φ26	D110*33	φ2.0-φ56
D16*13	φ1.0-φ3.6	D55*28	φ1.0-φ28	D120*33	φ2.0-φ60
D20*14	φ1.0-φ5.7	D60*30	φ1.0-φ30	D130*33	φ2.0-φ66
D20*17	φ1.4-φ6.0	D65*30	φ1.0-φ33	D140*33	φ2.0-φ70
D22*18	φ1.5-φ7.0	D75*30	φ1.0-φ38	D150*33	φ2.0-φ76
D25*18	φ3.0-φ9.0	D80*32	φ1.0-φ41	D160*33	φ2.0-φ80
D30*22	φ7.7-φ11.0	D85*32	φ1.0-φ43	D170*33	φ2.0-φ86
D35*25	φ6.7-φ18.3	D90*32	φ1.0-φ46	D180*33	φ2.0-φ90

*Customized sizes are accepted.

III.Advantages of old craftsman wire drawing dies:

1. Good wear resistance: Tungsten carbide possesses high wear resistance, which could guarantee long-term work of drawing within any drawn amount and ensure the size and precision of products.
2. Excellent polishing: Carbide enjoys good polishing, and the die hole can be processed to the degree of mirror, thus ensuring high-quality of metal drawn surface.
3. Small adhesion: In the drawing process, the drawing die keeps little adhesion with metal processed, thereby enhancing the durability of drawing die and making processed material acquire high-quality gloss finish for surface.
4. Small friction coefficient: In the drawing process, smaller frictional resistance means less the power loss, thus enhancing overall efficiency.
5. High coefficient of thermal conductivity: In the drawing process, the generated heat can be conducted away very well.
6. Good corrosion resistance: This property is superior in the wet lubricated stretch, especially in the acidic lubricated stretch.

IV.Application of wire drawing dies:

1. Steel wire and stainless steel wire
2. Copper wire
3. Alu wire and tungsten wire
4. Various kinds of ferrous and non-ferrous metal wire